Effect of oxygen addition on the hydrogen production from ethanol steam reforming in a Pd–Ag membrane reactor

In this communication, a porous stainless steel (PSS) tube was electrolessly plated into Pd–Ag membrane reactor which was used for separating hydrogen produced in an ethanol steam reforming reaction with the addition of oxygen, which has not been reported before. Palladium and silver were deposited on porous stainless steel tube via the sequential electroless plating procedure with an overall film thickness of 20 μm and Pd/Ag weight ratio of 78/22. Ethanol–water mixture (n_water/n_ethanol = 1 or 3) and oxygen (n_oxygen/n_ethanol = 0.2 or 0.7) were fed concurrently into the membrane reactor packed with MDC-3. The reaction temperatures were set at 593–723 K and the pressures 3–10 atm. The effect of oxygen addition plays a vital role on the ethanol steam reforming reaction, especially for the Pd–Ag membrane reactor in which a higher flux of hydrogen is required. If oxygen in the feed is not sufficient, it would be possible that steam reforming reaction prevails. Inversely, high O₂ addition will shift the reaction scenario to be partial oxidation dominating, and selectivity of CO₂ increases with increasing oxygen feed. At high pressure, autothermal reaction of ethanol would be easily reached.     

Hydrogen Production by Steam Reforming of Ethanol: A Two Step Process

A two-layer fixed-bed catalytic reactor for hydrogen production by steam reforming of ethanol is proposed. In this reactor ethanol is first converted to acetaldehyde over a Cu-based catalyst and then acetaldehyde is converted to a hydrogen-rich mixture over a Ni-based catalyst. It is shown that the use of such type of reactor prevents coke formation and provides hydrogen yields closed to equilibrium.     

助剂对负载型镍催化剂重整活性和抗积炭性能的影响

应用ＸＲＤ和催化活性评价手段，考察了助剂对Ｃ２重整制合成气的负勒型Ｎｉ催化剂的重整活性和其抗积炭性能的影响。实验结果表明，ＮｉＯ在γ－Ａｌ２Ｏ３表面上最大分散量随ＭｇＯ、Ｌａ２Ｏ３助剂的添加没程度地增大，助剂能影响负载型Ｎｉ催化剂 论性能，ＭｇＯ、Ｌａ２Ｏ３的添加对改善Ｎｉ催化剂的重整活性和抗积炭性能有明显效果，并与助剂的种类添加次序有关。     

甲醇自热重整制氢反应分析

甲醇自热重整制氢反应是车载燃烧电池氢源的理想方式,本文应用ZnO/Cr2O3催化剂MOR－67上的宏观动力学,模拟分析了甲醇自热重整制反应器,合适的反应器为绝热径向反应器,对于本反应器一维拟均相模拟结构表明;适宜的水／醇比为2（常压）或3（低压）;压力0．2MPa-0.3MPa。     

甲烷干气重整反应中镍基催化剂上表面积碳研究(英文)

镍基催化剂上积碳是甲烷干气重整反应急需解决的关键问题。实验采用ＴＰＳＲ、ＴＰＤ、ＸＰＳ和脉冲反应等方法系统研究了镍基催化剂表面积碳的形态和特点。热力学研究表明,在５７３ Ｋ到１２７３ Ｋ的温度范围内,催化剂的表面积碳是不可避免的。ＴＰＳＲ、ＸＰＳ和ＴＰＤ研究表明,甲烷在催化剂表面裂解将形成至少三种碳物种：Ｃα、Ｃβ和Ｃγ。这三种碳物种具有不同的表面迁移能力、热稳定性和反应活性。其中,Ｃα物种在甲烷干气重整反应中是一种非常活泼和重要的中间体;Ｃγ物种则可能是表面积碳的前驱物：部分脱氢的Ｃβ物种能够与Ｈ２或ＣＯ２反应生成ＣＨ４或ＣＯ。     

CO2预处理操作条件对Ni-Co双金属催化剂性能与结构的影响

与传统H₂预处理方法相比,新型H₂+CO₂预处理方法（HCD）能显著提升Ni-Co双金属催化剂的沼气重整活性及抗积碳性能. 考察了HCD预处理操作条件对催化剂性能与结构的影响. 较好的HCD预处理操作条件是在催化剂经H₂处理之后,再用175-200 mL·min^-1的原料气CH₄/CO₂（比例为0：10）在780-800 ℃下还原0.5-1h. 在优化预处理操作条件下对催化剂进行了511 h的耐久性考察,并运用X射线衍射（XRD）、热重-差示扫描量热（TG-DSC）、透射电子显微镜（TEM）等手段对耐久性测试后的催化剂进行了表征. 在511 h 的稳定性实验内,CH₄、CO₂转化率,H₂、CO选择性及H₂/CO体积比分别高达96%、97%,98%、99%及0.98. 催化剂在测试期间的平均积碳速率仅为0.2 mg·g^-1·h^-1. 在该预处理操作参数下,催化剂拥有最好的综合性能和良好的耐久性.     

载体对担载Ni催化剂甲烷与二氧化碳重整反应活性的影响

制备了 Zr O2 、Mg O改性的 Al2 O3、Ti O2 复合载体 ,并应用 X-射线粉末衍射 (XRD)、比表面积测定、扫描电镜 (SEM)等手段进行了表征 .结果表明 ,这些氧化物在 Al2 O3上的晶粒尺寸小、比表面积大 ,分散较好 ,而在Ti O2 上的分散性较差 .对经 10 73K焙烧的 Mg O/ Ti O2 ,还发现部分 Ti O2 载体由锐钛矿变为金红石 ,同时生成Mg Ti O3 新相 .考察了载体对 Ni催化剂的 CH4与 CO2 重整反应活性的影响 ,其次序为 :Mg O/ Al2 O3>Zr O2 /Al2 O3>Al2 O3>Mg O >Zr O2 >Ti O2 >Mg O/ Ti O2 . Ti O2 及 Mg O/ Ti O2 担载 Ni催化剂的低活性可能与 Ti O2 本身的还原性有关     

几种低碳醇在Pt／TiO2上的光催化产氢速率的研究

主要考察了无氧条件下低碳醇（甲、乙、丙醇）在Pt/TiO2表面光催化重整反应制氢。深入探讨了几种低碳醇与其放氢速率的构-效关系,提出了低碳醇在Pt/TiO2光催化剂表面吸附态的模型。